Pengaruh Fraksi Serat terhadap Kekuatan Impak pada Lapisan Luar Komposit Honeycomb
Keywords:
impact energy, volume fraction, impact strength, honeycomb composite, coconut coir fibreAbstract
Sandwich composites with a bamboo honeycomb core and coconut coir fibre face plates offer an alternative for lightweight structures that must absorb impact energy. This study examines the effect of coir fibre volume fraction in the face plate on the impact energy and impact strength of the composite. Fibres were alkali-treated in sodium hydroxide for one hour, then moulded with epoxy resin into 2 mm face plates at volume fractions of 30%, 40% and 50%. The core was assembled from bamboo strips into hexagonal cells of 10 mm cell side, 20 mm wall height and 1 mm wall thickness. Testing followed the Izod method of ASTM D256 with three specimens per fraction, and impact strength was taken as absorbed energy divided by the 136 mm² cross-section. Mean impact energy reached 6.93 J at 30%, 9.67 J at 40% and 7.50 J at 50%, equivalent to impact strengths of 0.0510, 0.0711 and 0.0551 J/mm². Scatter was wide, with standard deviations of 2.52, 5.80 and 3.32 J, and one-way analysis of variance gave F(2,6) = 0.37 (p = 0.71). The 40% composition is therefore best read as a working indication that needs confirmation with more specimens and tighter process control.
References
Nurfatihayati, N., Alfarisi, C.D., Drastinawati, D., Khairat, K., Akbar, M. dan Maharani, C., 2023. Pembuatan komposit dari serat sabut kelapa dan resin polyester sebagai material untuk helm. Journal of Bioprocess, Chemical and Environmental Engineering Science, 4 (2), pp.57-64.
Tanjung, I., 2022. Analisis morfologi serat dan kekuatan impak bahan komposit berpenguat serat pinang (Areca catechu) yang telah dilakukan perbaikan sifat fisik. VOCATECH: Vocational Education and Technology Journal, 4 (1), pp.1-7.
Palese, K.G., Shofwan, M., Cahyono, D. dan Intan, R.P., 2025. Analisis perbandingan efisiensi struktur baja wide flange dengan honeycomb pada proyek pembangunan Ballroom Whiz Trawas di Mojokerto. Jurnal Anggapa, 4, pp.9-16.
Fachrudin, A.R., Astuti, F.A.F., Dani, A. dan Firdaus, A.H., 2025. Analisis komposit hybrid serat kelapa dan kulit jagung terhadap kekuatan impak sebagai material bumper. Pendas: Jurnal Ilmiah Pendidikan Dasar, 10 (4), pp.276-284.
Zikri, Sidabutar, G.W.T. dan Putra, R., 2025. Pengaruh massa serat kelapa pada material komposit terhadap kekuatan puntir. Zona Mesin, 15 (2), pp.38-44.
Saputra, R., Kardiman, Santoso, D.T. dan Imran, A.I., 2022. Analisis sifat mekanis dan sifat fisis pada komposit serat sabut kelapa serat bambu matriks epoxy sebagai material bumper mobil. Jurnal Rekayasa Mesin, 17 (1), pp.37-48.
Hastuti, S., Budiono, H.S., Ivadiyanto, D.I. dan Nahar, M.N., 2021. Peningkatan sifat mekanik komposit serat alam limbah sabut kelapa (cocofiber) yang biodegradable. Reka Buana: Jurnal Ilmiah Teknik Sipil dan Teknik Kimia, 6 (1), pp.30-37.
Widhiansyah, D.A. dan Widjanarko, 2025. Effect of alkali treatment and volume fraction on the impact strength of coconut fiber composite (cocofiber)-epoxy. J-MEEG: Jurnal Teknik Mesin, 4 (1), pp.359-364.
Sasria, N., Pradypta, P.D., Laksono, A.D. dan Rohimsyah, F.M., 2022. Composite manufacturing of coir fiber-reinforced polyester as a motorcycle helmet material. JMPM: Jurnal Material dan Proses Manufaktur, 6 (1), pp.48-56.
Zarviansyah, P., Juanda dan Pranandita, N., 2023. Pengaruh variasi fraksi volume komposit serat sabut kelapa matrik polyester terhadap kekuatan tarik. Jurnal Inovasi Teknologi Terapan (JITT), 1 (2).
Muhammad, Putra, R., Islami, N., Hafli, T. dan Malik, A., 2023. Pengaruh fraksi volume serat terhadap kekuatan tarik komposit serat daun nanas dan sabut kelapa dengan polyester bening 108. Malikussaleh Journal of Mechanical Science and Technology, 7 (1), pp.68-73.
Manalu, E.F. dan Yulianto, D., 2025. Pengaruh variasi campuran serat ijuk dan serat sabut kelapa dengan matriks epoxy terhadap kekuatan mekanik komposit. Action Research Literate, 9 (5).
Sya'roni, M.E.H. dan Ningsih, T.H., 2021. Pengaruh fraksi volume komposit bambu terhadap kekuatan tekan dengan metode hand lay-up dan vacuum bag. Jurnal Teknik Mesin Unesa, 9 (3), pp.69-74.
ASTM International, 2023. Standard test methods for determining the Izod pendulum impact resistance of plastics (ASTM D256-23e1). West Conshohocken, PA: ASTM International.
Wiranegara, C.B., Salahudin, X. dan Hastuti, S., 2022. Pemanfaatan serat alam dan serat sintetis sebagai material bilah Horizontal Axis Wind Turbine. Dalam: SENASTER Seminar Nasional Riset Teknologi Terapan, 3 (1).
Musanif, I. dan Dosoputranto, E., 2018. Effect of fiber length against hardness and composite impact coconut fiber-polyester resin. International Research Journal of Engineering and Technology (IRJET), 5 (2), pp.1178-1181.
Haryoszi, H., 2025. Pengaruh fraksi volume serat tebu dan variasi perendaman NaOH terhadap matrik polyester dengan kekuatan uji impak. Skripsi. Bangka Belitung: Politeknik Manufaktur Negeri Bangka Belitung.
Syarief, A. dan Fauzi, D.H., 2023. Pengaruh fraksi volume hybrid composite bulu itik dan serat purun tikus bermatrik polyester terhadap kekuatan tekan dan bentuk patahan. JTAM Rotary, 5 (2), pp.93-104.